ISO-7214 JIS-K6767 K6382 Foam Rubber Repeated Compression Tester For Lab
After accurately measure the thickness of the test piece, then place it in the compression plate of the testing machine, compressing the test piece 60 times at a rate of 60 times per minute, compressing the test piece by 50%, the reciprocating compression is up to 80,000 times, and after 30 minutes at normal temperature, the thickness is measured to convert the compression deformation rate.
Standard: ISO-7214, JIS-K6767, K6382
Technical Parameters:
Compression stroke: 0~50mm
Compression rate: 60cpm
Platen spacing: 200mm
Test piece size: 200 × 200mm
Platen area: 30×30cm
Upper pressure plate: V-type exhaust groove distance: 19 × 19mm
Lower pressure plate: 289 venting holes, hole spacing: 19mm
Motor: 1/3HP
Counter: LCD, 0~999999
Volume: 60 × 40 × 75cm
Weight: 102kg
Power supply: 1∮AC220, 5A
ISO-7214 JIS-K6767 K6382 Foam Rubber Repeated Compression Tester For Lab
After accurately measure the thickness of the test piece, then place it in the compression plate of the testing machine, compressing the test piece 60 times at a rate of 60 times per minute, compressing the test piece by 50%, the reciprocating compression is up to 80,000 times, and after 30 minutes at normal temperature, the thickness is measured to convert the compression deformation rate.
Standard: ISO-7214, JIS-K6767, K6382
Technical Parameters:
Compression stroke: 0~50mm
Compression rate: 60cpm
Platen spacing: 200mm
Test piece size: 200 × 200mm
Platen area: 30×30cm
Upper pressure plate: V-type exhaust groove distance: 19 × 19mm
Lower pressure plate: 289 venting holes, hole spacing: 19mm
Motor: 1/3HP
Counter: LCD, 0~999999
Volume: 60 × 40 × 75cm
Weight: 102kg
Power supply: 1∮AC220, 5A